性能 Properties |
单位 Unit |
典型值 Typical value |
|
密度Density |
g/cm3 |
0.905±0.005 |
|
厚度 Thickness |
µm |
2.2 ～ 15 |
|
抗拉强度Tensile Strength |
纵向MD (MPa) |
≥100 |
|
断裂伸长率Elongation at Break |
纵向MD (%) |
20～200 |
|
弹性模量Elastic modulus |
纵向MD (MPa) |
2800 |
|
热收缩率Heat Shrinkage |
纵向MD (%) |
≤5 ( 120°C, 10min) |
|
湿润张力Wetting tension |
mN/m |
38 (电晕处理面Corona treated side) |
|
表面粗糙度Surface roughness |
µm |
0.08 |
|
熔点Melting point |
℃ |
172 |
|
体积电阻率Volume resistivity |
Ω.m |
＞1015 |
|
介电强度Break-dowm voltage |
V/µm |
≥350 ( 23°C, DC ) |
|
相对介电常数Dielectric constant |
2.2 (20℃，1KHz) |
|
|
介电损耗因数Dissipation Factor |
≤4×10-4 (20℃，1KHz ) |
|
|
RC值 |
ΩF |
≥5×104 |
金属化聚酯薄膜(MPET Film)：
|
性能 Properties |
单位 Unit |
典型值 Typical value |
||
|
密度Density |
g/cm3 |
1.4 |
||
|
厚度 Thickness |
µm |
＜5 |
5～12 |
≥12 |
|
抗拉强度Tensile Strength |
纵向MD (MPa) |
≥84 |
≥108 |
≥120 |
|
断裂伸长率Elongation at Break |
纵向MD (%) |
≥22 |
≥33 |
≥44 |
|
弹性模量Elastic modulus |
纵向MD (MPa) |
3500 |
||
|
介电强度Break-dowm voltage |
V/µm |
≥200 ( 23°C, DC ) |
≥250 ( 23°C, DC ) |
|
|
热收缩率Heat Shrinkage |
纵向MD (%) |
≤2.5 ( 150°C, 10min) |
||
|
表面粗糙度Surface roughness |
µm |
0.095 |
||
|
熔点Melting point |
℃ |
256 |
||
|
体积电阻率Volume resistivity |
Ω.m |
＞1015 ( 23°C, 相对湿度Humidity 50%) |
||
|
相对介电常数Dielectric constant |
3.2 (20℃，1KHz) |
|||
|
介电损耗因数Dissipation Factor |
- |
≤60×10-4 (20℃，1KHz ) |
||
|
RC值 |
ΩF |
≥1×104 |
||
n 包装
|
Ø 膜卷用塑料袋包装，抽真空后放入干燥剂热封 Ø 塑料包装袋外贴标签标明型号，厚度，宽度，留边宽度和电阻 Ø 塑料袋外面用纸箱包装 Ø 纸箱外面用木箱包装或者加固纸箱 |
|
n 储存
|
Ø 金属化膜在使用之前应该按原包装保存。环境温度应该控制在5～35℃，湿度小于85%RH。 Ø 金属层暴露在潮气中会很容易发生氧化。因此，包装打开后，膜卷应该尽快使用。 Ø 建议打开包装的膜卷应该保存的温度条件是15～25℃，湿度小于60%RH。 Ø 金属化膜若保持原密封包装，并储存在如上所述的环境下，那么其储存期限可以满足下列条件： 铝金属化薄膜：从交付日起12个月。 锌铝金属化薄膜：因为锌相当不稳定，储存的期限（从交付日起）取决薄膜的电阻： ≤10 Ω/□：6个月 10 ～30Ω/□：3个月 ＞30Ω/□：1个月
|
|